Adsorption-Engineered Hydrocarbon Ionomers for Durable Proton-Exchange Membrane Fuel Cells
.png){kind=icon}
OA
AI
H
K
S
H
C
J
L
D
S
J
S
P
E
Y
DOI：10.1002/adma.74561.png)
.png){kind=icon}
.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Reducing reliance on perfluoroalkyl substances (PFAS) in proton-exchange membrane fuel cells requires hydrocarbon ionomers that combine high performance with long-term durability, a persistent challenge in catalyst-layer design. Here, we identify oxidation-driven ionomer-catalyst interfacial degradation as a dominant failure pathway in hydrocarbon ionomer-bonded cathodes and introduce an adsorption-engineering strategy to overcome this limitation. The comparison of a commercial sulfonated poly(phenylene) (Pemion) with structurally engineered sulfonated poly(fluorene)s demonstrated that electrode durability is governed by the interplay between ionomer adsorption strength and resistance to oxidative degradation on carbon-supported Pt catalysts. A poly(fluorene) ionomer with mobile alkyl sulfonic acid groups forms resilient interfaces, delivering 1.28 A cm−2 at 0.65 V under fully humidified H2/air conditions (80°C and 150 kPaabs), comparable to Pemion. After 90,000 accelerated potential cycles, the poly(fluorene)-bonded cathode exhibits significantly improved durability, with only 29% performance loss compared to 58% for Pemion; further molecular refinement reduces the loss to 17%, approaching that of Nafion-bonded cathodes (14%). These findings establish adsorption-engineered ionomer design that decouples interfacial anchoring from oxidative degradation as a general strategy for achieving durable, high-performance PFAS-free PEM fuel cell electrodes.
Keywords:
durability
electrode
ionomer
ionomer adsorption
materials science
proton exchange membrane fuel cell
sulfonic acid