Calculations on compact disc cracking
.png){kind=icon}
OA
AI
DOI：10.1098/rsta.2020.0292.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
The Griffith equation for brittle cracking has three problems. First, it applies to an infinite sheet whereas a laboratory test sample is typically near 100 x 100 mm. Second, it describes a central crack instead of the more dangerous and easily observable edge crack. Third, the theory assumes a uniform stress field, instead of tensile force application used in the laboratory. The purpose of this paper is to avoid these difficulties by employing Gregory's solution in calculating the crack behaviour of PMMA (Poly Methyl Meth Acrylate) discs, pin loaded in tension. Our calculations showed that axial disc loading gave nominal strengths comparable with Griffith theory, but the force went to zero as the crack fully crossed the disc, fitting experimental results. Off-axis loading was more interesting because the predicted strength was lower than in axial testing, but also gave unexpected behaviour at short crack lengths, where nominal strength did not rise indefinitely but dropped as crack length went below D/10, quite different from Griffith, where strength rose continuously as cracks were shortened. Such off-axis loading leads to a size effect in which larger discs are weaker, reminiscent of the fine fibre strengthening phenomenon reported in Griffith's early paper (Griffith 1921 Phil. Trans. R. Soc. Lond. A 221, 163-198.doi:10.1098/rsta.1921.0006)). This article is part of a discussion meeting issue 'A cracking approach to inventing new tough materials: fracture stranger than friction'.
Keyword:
cracking
Griffith equation
compact disc test
size effect
期刊
P
IF:
3.7
论文数:
7.8K
被引数:
2.8W
机构
暂无机构信息
引用论文
Nucleolar organizer regions of megakaryocytes in chronic myeloproliferative disorders慢性骨髓增殖性 disorders 中巨核细胞的核仁组织区
PREAI
分享收藏
Fluorine containing amino acids and their derivatives. 7. Synthesis and antitumor activity of α- and γ-substituted methotrexate analogs.png)
Tetrahedron
TetrahedronIF0
PREAI
分享收藏分享收藏Role of oxygen vacancy tuning in EBPVD deposited LaxCe1−xO2−δfilms in high temperature oxidation protectionRSC Advances
RSC AdvancesIF0
PREAI
分享收藏
查看更多内容