Cracks in functionally graded materials
.png){kind=icon}
OA
AI
DOI：10.1016/S0921-5093(03)00582-3.png)
.png){kind=icon}
.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
The weight function method is described to analyze the crack growth behavior in functionally graded materials and in particular materials with a rising crack growth resistance curve. Further, failure of graded thermal barrier coatings (TBCs) under cyclic surface heating by laser irradiation is modeled on the basis of fracture mechanics. The damage of both graded and non-graded TBCs is found to develop in several distinct stages: vertical cracking --> delamination --> blistering --> spalling. This sequence can be understood as an effect of progressive shrinkage due to sintering and high-temperature creep during thermal cycling, which increases the energy-release rate for vertical cracks which subsequently turn into delamination cracks. The results of finite element modeling, taking into account the TBC damage mechanisms, are compatible with experimental data. An increase of interface fracture toughness due to grading and a decrease due to ageing have been measured in a four-point bending test modified by a stiffening layer. Correlation with the damage observed in cyclic heating is discussed. It is explained in which way grading is able to reduce the damage. (C) 2003 Published by Elsevier B.V.
Keyword:
FGM
fracture mechanics
R-curve
residual stresses
TBC
AI总结
对已上传原文的论文进行重点信息的提取，主要内容包括：简要概述、研究摘要、背景介绍、关键亮点、图文解析、展望与总结。
期刊
机构
暂无机构信息
引用论文
Laser induced creep and fracture in ceramics.png)
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSINGIF7
PREAI
分享收藏
The hand and the object: the role of posterior parietal cortex in forming motor representations
PREAI
分享收藏Analysis of an industrial continuous slurry reactor for ethylene–butene copolymerizationPolymerOAAI
PolymerIF0
OAAI分享收藏分享收藏
查看更多内容