Electro-Chemo-Mechanical Evolution at the Garnet Solid Electrolyte-Cathode Interface
.png){kind=icon}
PRE
AI
DOI：10.1021/acsami.4c04713.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Solid-state batteries promise higher energy density and improved safety compared with lithium-ion batteries. However, electro-chemomechanical instabilities at the solid electrolyte interface with the cathode and the anode hinder their large scale implementation. Here, we focus on resolving electro-chemo-mechanical instability mechanisms and their onset conditions between a state-of-the-art cathode, LiNi0.6Mn0.2Co0.2O2 (NMC622), and the garnet Li7La3Zr2O12 (LLZO) solid electrolyte. We used thin-film NMC622 on LLZO pellets to place the interfacial region within the detection depth of the X-ray characterization techniques. The experimental probes of the near-interface region included in operando X-ray absorption spectroscopy and ex situ focused ion beam scanning electron microscopy. Electrochemical degradation was not observable during cycling at room temperature with 4.3 V versus Li/Li+ charge voltage cutoff, or with stepwise potentiostatic hold up to 4.1 V versus Li/Li+. In contrast, secondary phases including reduced transition metal species (Ni2+, Co2+) were found after cycling up to 4.3 V versus Li/Li+ at 80 degrees C and during potentiostatic hold at 4.3 V versus Li/Li+ (Ni2+). Intergranular cracks between NMC622 grains and delamination at the NMC622|LLZO interface occurred readily after the first charge. These interface reaction products and mechanical failure lowered the capacity and cell efficiency due to partial loss of the NMC622 phase, partial loss of contact at the interface, and a higher polarization resistance. Electrochemical instability between delithiated NMC622 and LLZO could be mitigated by using a low charge voltage cutoff or cycling at lower temperature. Ways to engineer the mechanical properties to avoid crack deflection and delamination at the interface are also discussed for enhancing mechanical stability.
Keyword:
solid-state battery
LLZO
lithium nickel manganesecobalt oxide
NMC
X-ray absorption spectroscopy
FIB-SEM
期刊
IF:
8.2
论文数:
6.1W
被引数:
38.7W
机构
引用论文
Fundamentals of inorganic solid-state electrolytes for batteries电池用无机固态电解质基础.png)
NATURE MATERIALS
NATURE MATERIALSIF38.5
PREAI
分享收藏Understanding the Surface Regeneration and Reactivity of Garnet Solid-State Electrolytes了解石榴石固态电解质的表面再生和反应性ACS ENERGY LETTERS
OAAI
ACS ENERGY LETTERSIF18.2
OAAI分享收藏Li Penetration in Ceramic Solid Electrolytes: Operando Microscopy Analysis of Morphology, Propagation, and Reversibility陶瓷固体电解质中的Li渗透: 形态，传播和可逆性的Operando显微镜分析MATTEROAAI
MATTERIF17.5
OAAI分享收藏Structure, Chemistry, and Charge Transfer Resistance of the Interface between Li7La3Zr2O12 Electrolyte and LiCoO2 CathodeLi7La3Zr2O12电解质与LiCoO2阴极之间的界面的结构，化学和电荷转移电阻OAAI
OAAI分享收藏Operando measurements of dendrite-induced stresses in ceramic electrolytes using photoelasticity使用光弹性对陶瓷电解质中的枝晶诱导应力进行Operando测量MATTER
MATTERIF17.5
PREAI
分享收藏Mechanical instability of electrode-electrolyte interfaces in solid-state batteries固态电池中电极-电解质界面的机械不稳定性
PREAI
分享收藏分享收藏
查看更多内容