Energy-Efficient Capacitive Deionization through Electrode Modification and Process Development
.png){kind=icon}
PRE
AI
DOI：10.1021/acssuschemeng.4c09320.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Electrochemical separation technologies, such as capacitive deionization (CDI), are promising for addressing global energy and water challenges. However, there is a need to improve the performance, better understand property-performance relationships, and evaluate the longevity of CDI electrodes. This study explores the chemical modification of electrodes and the adjustment of CDI operating parameters. Results indicate that nitric acid (HNO3) conditioning of activated carbon cloth (ACC) electrodes removes metal oxides, introduces oxygen and nitrogen functionalities, and increases the specific capacitance (16% at 1 mV/s). Moreover, these changes in electrode properties positively impact device-level CDI performance. Through HNO3-conditioning of the ACC and tuning of the operational parameters, this work demonstrates higher electrosorption capacity (4.0x), greater charge efficiency (90% vs 24%), and lower energy consumption (3.8x). Despite these enhancements, limitations of the HNO3-conditioned ACC include decreased desorption kinetics and a 32% loss in electrosorption capacity after 200 cycles. Overall, this work provides guidance on using oxidative pretreatment via HNO3 to modify ACC electrodes for CDI and evaluates the trade-offs associated with varying operational parameters.
Keyword:
separation
electrosorption
activated carbon
pretreatment
flow rate
half-cycle time
期刊
IF:
7.3
论文数:
1.7W
被引数:
10.7W
机构
引用论文
Catalyst Deactivation and Its Mitigation during Catalytic Conversions of Biomass生物质催化转化过程中催化剂的失活及其缓解.png)
ACS CATALYSIS
OAAI
ACS CATALYSISIF13.1
OAAI分享收藏Facile Fabrication of NiCoAl-Layered Metal Oxide/Graphene Nanosheets for Efficient Capacitive Deionization DefluorinationNiCoAl层状金属氧化物/石墨烯纳米片的简易制备，用于高效的电容去离子脱氟
PREAI
分享收藏Capacitance limits of high surface area activated carbons for double layer capacitors用于双层电容器的高表面积活性炭的电容极限CARBON
CARBONIF11.6
PREAI
分享收藏
查看更多内容