Experimental determination of the isothermal sections and the liquidus surface projection of the Mo-Si-Cr ternary system
.png){kind=icon}
PRE
AI
H
C
C
Z
DOI：10.1016/j.jallcom.2022.166164.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
The isothermal sections at 1200 and 1000 degrees C and the liquidus projection of the Mo-Cr-Si system have been experimentally determined based on the microstructures, the phase structure analyses and the phase constitutions of the as-cast and the isothermally heat treated alloys in whole composition range, using scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) and X-ray dif-fraction (XRD) techniques. In the isothermal section at 1000 and 1200 degrees C, five three-phase regions and ten two-phase regions were derived, and no ternary compounds were observed. Nine primary solidification regions and six univariant reaction lines were deduced based on the study on the solidification processes of the as-cast alloys in the liquidus surface projection. In addition, the stoichiometry compounds Mo5Si3 and alpha Cr5Si3 are the phases of the same structure (W5Si3-type) but different compositions, forming two inter-metallic compounds Mo-rich Mo(Cr)(5)Si-3 and Cr-rich Cr(Mo)(5)Si-3. The present experimental results could be used for the further thermodynamic assessment of the Mo-Si-Cr ternary system, and be helpful for the database development of the multi-components Nb/Mo-Si-based superalloy system. (C) 2022 Elsevier B.V. All rights reserved.
Keywords:
The Mo-Cr-Si ternary system
Isothermal sections
Liquidus projection
Solidification paths
Phase diagram
Microstructure