Granular nanostructures and magnetic properties of FePt-C/FePt-SiO2 films
.png){kind=icon}
PRE
AI
L
刘
K
S
DOI：10.1016/j.jallcom.2015.08.106.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
FePt-C, FePt-SiO2 and FePt-C/FePt-SiO2 films with different segregants concentration on glass substrate with polycrystalline MgO underlayer have been successfully fabricated by magnetron sputtering system. It was found that the FePt-C films had larger coercivity(H-c), chemical order parameter(S) and smaller diameter of the local interaction zone(D-n) but wider magnetic coercive force distribution(Delta H-c/H-c) than that of the FePt-SiO2 films. By using FePt-C/FePt-SiO2 bilayer structure, the low D-n and Delta H-c/H-c were obtained. FePt-C30vol%(4 nm)/FePt-SiO(2)45vol%(4 nm) film with Hc higher than 29 kOe and columnar FePt grains of 10 nm in diameter and 13 nm in height were obtained, which would be very suitable for heat assisted magnetic recording media. (C) 2015 Elsevier B.V. All rights reserved.
Keywords:
Magnetic films and multilayers
Magnetic measurements
Thin films