High-performance AISI 316L by microstructure engineering
.png){kind=icon}
PRE
AI
DOI：10.1016/j.msea.2025.148036.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
In this work, a high-performance AISI 316L was produced by microstructure engineering. Asymmetric turned rolling (ATR) followed by back-annealing at 900 degrees C for 10, 30, 60, and 120 min was used to achieve a unique microstructure. The results showed that, in the 900-10 and 900-30 samples, there was a microstructure consisting of a thin recrystallized surface layer and a deformed non-surface area. By increasing the annealing time to 60 and 120 min, the reversion of strain-induced martensite (SIM) and recrystallization of deformed austenite has occurred in the entire microstructure. It was found that with increasing the back-annealing duration, the intensity of Rotated Cube {001}<110> (shear texture) and Cube {001}<100> (recrystallization texture) components was decreased and increased, respectively, due to the occurrence of recrystallization in the microstructure. The hardness, yield strength, and tensile strength of the 900-10 sheet were respectively 1.9 (264 HV vs. 142 HV), 2.4 (527 MPa vs. 216 MPa), and 1.4 (825 MPa vs. 588 MPa) times higher than those of the solution-treated steel owing to the refinement of the austenite grains as well as the presence of deformed gamma in the non-surface regions. An obvious recovery of work-hardening rate (WHR) was observed in the second stage of the back-annealed sheets owing to the formation of SIMs and deformation twins during tensile testing. The slope of the WHR curve in the second stage was different for the back-annealed samples at different holding times. With increasing the back-annealing time, the failure mode changed from shear ductile to fully ductile.
Keyword:
Austenitic stainless steel
Asymmetric turned rolling
Back-annealing
Microstructure engineering
Texture
Mechanical behavior
期刊
机构
引用论文
Microstructural and crystallographic aspects of conventional and asymmetric rolling processes.png)
ACTA MATERIALIA
ACTA MATERIALIAIF9.3
PREAI
分享收藏Effect of cold rolling route and annealing on the microstructure and mechanical properties of AISI 316 L stainless steel冷轧路线和退火对AISI 316 L不锈钢组织和力学性能的影响
PREAI
分享收藏High-temperature annealing behavior of cold-rolled electrolytic tough-pitch copper冷轧电解韧铜的高温退火行为HELIYON
OAAI
HELIYONIF3.6
OAAI分享收藏Comparison of conventional and severe shot peening effects on the microstructure, texture, roughness, hardness, and electrochemical behavior of austenitic stainless steelHELIYONOAAI
HELIYONIF3.6
OAAI分享收藏The synergistic effect of grain boundary and grain orientation on micro-mechanical properties of austenitic stainless steel晶界与晶粒取向对奥氏体不锈钢微观力学性能的协同作用
PREAI
分享收藏
查看更多内容