Hydroxyapatite formation from cuttlefish bones: kinetics

doi:10.1007/s10856-010-4115-4

2010-06-22

Hrvoje Ivanković *

Emilija Tkalčeć

Sandi Orlić

Gloria Gallego Ferrer

Zdravko Schauperl

DOI：10.1007/s10856-010-4115-4

原文链接

原文求助

摘要

En 中文

Highly porous hydroxyapatite (Ca(10)(PO(4))(6)center dot(OH)(2), HA) was prepared through hydrothermal transformation of aragonitic cuttlefish bones (Sepia officinalis L. Adriatic Sea) in the temperature range from 140 to 220A degrees C for 20 min to 48 h. The phase composition of converted hydroxyapatite was examined by quantitative X-ray diffraction (XRD) using Rietveld structure refinement and Fourier transform infrared spectroscopy (FTIR). Johnson-Mehl-Avrami (JMA) approach was used to follow the kinetics and mechanism of transformation. Diffusion controlled one dimensional growth of HA, predominantly along the a-axis, could be defined. FTIR spectroscopy determined B-type substitutions of CO(3) (2-) groups. The morphology and microstructure of converted HA was examined by scanning electron microscopy. The general architecture of cuttlefish bones was preserved after hydrothermal treatment and the cuttlefish bones retained its form with the same channel size (similar to 80 x 300 mu m). The formation of dandelion-like HA spheres with diameter from 3 to 8 mu m were observed on the surface of lamellae, which further transformed into various radially oriented nanoplates and nanorods with an average diameter of about 200-300 nm and an average length of about 8-10 mu m.

Keyword:

CARBONATED HYDROXYAPATITE

CRYSTALLIZATION KINETICS

CRYSTAL STRUCTURE

THIN-FILMS

SCAFFOLDS

PHOSPHATE

ARAGONITE

GROWTH

TRANSFORMATION

CONVERSION