Layered Ni-MOFs with dual-ligand modulation: A high-rate-performance sulfur host for enhanced catalytic activity in lithium-sulfur batteries
.png){kind=icon}
PRE
AI
Y
Z
J
S
L
L
Y
J
DOI：10.26599/NR.2025.94908198.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Redox sluggishness and polysulfide dissolution in lithium-sulfur (Li-S) batteries arise from weak host with polysulfides interactions. Herein, ligand defects are controllably engineered within a two-dimensional (2D) Ni-based metal-organic frameworks (Ni-MOFs) that is epitaxially grown on rGO to afford ultrathin composite nanosheets. By precisely modulating the molar ratio of terephthalic acid to salicylic acid during solvothermal synthesis, a series of Ni-MOFs/rGO composites (denoted NPS/rGO) are obtained. The defective architecture simultaneously exposes a high density of open coordination sites and establishes continuous Li-ion diffusion pathways. Notably, NPS-3/rGO exhibits maximal long-chain lithium polysulfides (LiPSs) chemisorption as quantified (ultraviolet-visible (UV-vis)) and fastest liquid-liquid and liquid-solid redox kinetics (symmetric-cell cyclic voltammograms (CV) and potentiostatic nucleation). When evaluated as a sulfur host in Li-S coin cells, the S@NPS-3/rGO cathode effectively suppresses polysulfide shuttling. Consequently, the NPS-3/rGO cathode delivers 1493.4 mAh & centerdot;g-1 at 0.1 C, 683.6 mAh & centerdot;g-1 at 2 C and less than 0.049% capacity decay per cycle over 750 cycles at 1 C, even at 3.72 mg & centerdot;cm-2 and electrolyte/sulfur (E/S) ratio of 11.88 & micro;L & centerdot;mg-1, it retains 1002.8 mAh & centerdot;g-1 at 0.1 C. This work highlights the potential of dual-ligand-modulated, ultrathin defective MOFs/carbon hybrids for high-rate, long-life Li-S batteries.
Keywords:
metal-organic framework
two-dimensional (2D) ultrathin host
linker defect
synergistic catalysis
lithium-sulfur battery