Organized structures obtained from urethane/urea elastomers

M. H. Godinho

doi:10.1016/j.synthmet.2004.06.047

2004-12-01

PRE

DOI：10.1016/j.synthmet.2004.06.047

原文链接

原文求助

摘要

En 中文

In this work we address new results obtained with free thin flexible films (60-100 mum) of urethane/urea elastomers related to the formation of micro- and nano-patterns. The samples were synthesised from a polypropylene oxide-based prepolymer with three isocyanate terminal groups (PU) and polybutadienediol (PBDO) with different PBDO content of 30, 40 and 60 wt.% After casting and curing the films were exposed to UV radiation (lambda = 254 nm) and extracted with toluene. The dried films were studied by polarising optical microscopy (POM), small angle light scattering (SALS) and the surfaces exposed to UV radiation were analysed by means of atomic force microscopy (AFM). Before extraction with toluene a manometer-flat surface, characterized by a mean roughness value R-a = 0.59 nm, was obtained. The sample with 40 wt.% of PBDO, after exposed to UV and extracted with toluene shows a corrugated surface, with features mum-sized in all axes, resulting in a dramatic increase of the overall mean roughness. As the PBDO concentration decreases the free films surfaces show an increasing density of the structures observed and a decreasing characteristic peak-to-valley height. This work suggests that the PBDO/PU samples exposed to UV radiation can be nano to micromodulated by tuning the PBDO/PU relative content. These structures can be revealed with toluene from the original manometer-flat surface. (C) 2004 Published by Elsevier B.V.

Keyword:

urethane/urea elastomers

UV radiation

atomic force microscopy