Persistent MgB2 joints for react and wind magnets
.png){kind=icon}
OA
AI
DOI：10.1088/1361-6668/ad06c3.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Ultra-low resistance joints are a key technology enabling superconducting magnets to operate in persistent mode and to achieve the temporal stability required for nuclear magnetic resonance and magnetic resonance imaging (MRI) applications. High performance superconducting joints are manufactured routinely for Nb-Ti and Nb3Sn magnets, but technologies for joining other technological superconductors are still in the early stages of development. Here we report the use of a simple cold pressing and heat treatment procedure to fabricate persistent MgB2 joints with resistance values <10(-12) Omega between MgB2 wires that have already undergone the full wire reaction process. Trapped persistent currents of 172 A and 160 A were achieved under self-field and 1 T background field conditions respectively at a temperature of 20 K. This corresponds to a critical current ratio of 78% under these conditions, outperforming previously reported joints using fully reacted MgB2 wire. These findings are relevant for the development of commercial MRI magnets with MgB2 wires utilizing react and wind methods.
Keyword:
applied superconductivity
superconducting joints
magnesium diboride
期刊
IF:
4.2
论文数:
8.3K
被引数:
1.2W
机构
引用论文
Connect, converse, collaborate: Encountering belonging and forging resilience through creative practice连接、对话、协作：通过创造性实践体验归属感并塑造韧性OAAI
OAAI分享收藏Niobium-titanium (Nb-Ti) superconducting joints for persistent-mode operation用于持久模式操作的铌-钛 (nb-ti) 超导接头.png)
SCIENTIFIC REPORTS
OAAI
SCIENTIFIC REPORTSIF3.9
OAAI分享收藏Reprint of: Epidemiological serosurvey of Hepatitis B in China—Declining HBV prevalence due to Hepatitis B vaccinationVaccine
VaccineIF0
PREAI
分享收藏Superconducting joints using multifilament MgB2 wires for MRI applicationSCRIPTA MATERIALIA
SCRIPTA MATERIALIAIF5.6
PREAI
分享收藏Conceptual designs of conduction cooled MgB2 magnets for 1.5 and 3.0T full body MRI systems用于1.5和3.0T全身MRI系统的传导冷却MgB2磁体的概念设计OAAI
OAAI分享收藏
查看更多内容