Polymeric precursor for solution-processed amorphous silicon carbide
.png){kind=icon}
PRE
AI
DOI：10.1039/c5tc03169a.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Amorphous silicon carbide (a-SiC) films are deposited via solution-based processes using a polymeric precursor solution consisting of polydihydrosilane with pendant hexyl groups. Unlike conventional polymeric precursors, this polymer neither requires catalysts nor oxidation for its synthesis and cross-linkage. Therefore, our polymeric precursor provides sufficient purity for the fabrication of solution-processed semiconducting a-SiC. Polymer-to-ceramic conversion is systematically investigated under various pyrolysis temperatures ranging from 320 degrees C to 420 degrees C. The polymer primarily undergoes cross-linking at temperatures above 150 degrees C with increasing polymer fraction; this cross-linking is followed by carbon atoms being incorporated into an amorphous network at 380 degrees C. The incorporated carbon atoms in the film are predominantly in the sp(3)-bonding state with almost no amorphous graphite-like sp(2) C=C clusters, leading to marked changes in the film's properties. The conductivity values of the resulting a-SiC films are comparable with those of semiconducting a-SiC films prepared using vacuum-based deposition.
Keyword:
HIGH-TENSILE STRENGTH
GLOW-DISCHARGE
INFRARED-ABSORPTION
OPTICAL-PROPERTIES
H FILMS
SIC-H
FIBER
POLYCARBOSILANE
SILYLENE
CONVERSION
期刊
IF:
5.1
论文数:
2.0W
被引数:
8.0W
机构
引用论文
Intravenous Valproate Use in Bipolar II Disorder After Gastric Bypass Surgery胃 bypass 手术后双相 II 型障碍患者静脉注射丙戊酸盐的应用
PREAI
分享收藏Visual and Tactile Size Distortion in a Patient with Right Neglect右侧忽视患者中的视觉和触觉大小失认.png)
Neurocase
NeurocaseIF0
PREAI
分享收藏Quaternary and quinary molecular solids based on structural inequivalence and combinatorial approaches: 2-nitroresorcinol and 4,6-dichlororesorcinolIUCrJ
OAAI
IUCrJIF0
OAAI分享收藏
查看更多内容