Pressure-induced magnetic moment abnormal increase in Mn2FeAl and non-continuing decrease in Fe2MnAl via first principles
.png){kind=icon}
OA
AI
DOI：10.1038/s41598-017-16735-1.png)
.png){kind=icon}
.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
The magnetism of Fe2MnAl and Mn2FeAl compounds are studied by first principles. Evolutions of magnetic moment of Fe2MnAl display distinct variation trends under pressure, showing three different slopes at different pressure intervals, 0 similar to 100 GPa, 100 similar to 250 GPa, 250-400 GPa, respectively, and the moment collapses finally at 450 GPa. The magnetic moment of Mn2FeAl shows an increasing tendency below 40 GPa and decreases subsequently with pressure, and collapses ultimately at about 175 GPa. Such non-continuing decrease of Fe2MnAl originates from the unusual charge transfer of Fe and Mn and bond populations rearrangement of Fe-Fe and Mn-Fe, whereas the distinct moment evolution of Mn2FeAl is attributed to the complicated distributions of bond populations. The half-metallicity of the compounds can be maintained at low pressure, below about 100 GPa in Fe2MnAl and 50 GPa in Mn2FeAl. The magnetic moment collapse process didn't induce volume and bond length anomalies in the two compounds, the unique anomaly is the elastic softening behaviour in elastic constant c(44) and shear (G) and Young's (E) moduli of Fe2MnAl at 270 GPa, where the second moment collapse occurs.
Keyword:
FULL-HEUSLER ALLOYS
TRANSITION
METAL
Z=AL
AI总结
对已上传原文的论文进行重点信息的提取，主要内容包括：简要概述、研究摘要、背景介绍、关键亮点、图文解析、展望与总结。
期刊
IF:
3.9
论文数:
28.3W
被引数:
83.5W
机构
引用论文
Magnetic moment collapse induced axial alternative compressibility of Cr2TiAlC2 at 420 GPa from first principle.png)
SCIENTIFIC REPORTSOAAI
SCIENTIFIC REPORTSIF3.9
OAAI分享收藏XCII. Relations between the elastic moduli and the plastic properties of polycrystalline pure metalsXCII。多晶纯金属的弹性模量与塑性之间的关系
PREAI
分享收藏
分享收藏
查看更多内容