Process-induced matrix defects: Post-gelation
.png){kind=icon}
PRE
AI
DOI：10.1016/j.compositesa.2020.106007.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Formation of resin matrix defects is common during composites manufacturing. The mechanisms behind these defects depend on the state of the resin at the time of their formation. Process-induced matrix defects are commonly studied in the form of porosity before gelation, or matrix cracking after vitrification. The present study investigates defect formation when the thermoset resin is between gelation and vitrification. After gelation, the resin is in a rubbery state and does not flow. M this state, cure in a constrained geometry leads to internal stress development and potential formation of defects. An experimental setup was used which allowed direct visual observation of the resin behavior after gelation. It was found that post-gelation defect formation is driven by hydrostatic stress and the defect morphology is cure rate-dependent. An analytical approach to avoid post-gelation defects based on comprehensive material characterization and internal stress evolution calculations is proposed, and experimentally validated.
Keyword:
Polymer-matrix composites
Defects
Internal stress
Analytical modeling
AI总结
对已上传原文的论文进行重点信息的提取，主要内容包括：简要概述、研究摘要、背景介绍、关键亮点、图文解析、展望与总结。
期刊
IF:
8.9
论文数:
8.8K
被引数:
4.5W
机构
引用论文
Multiscale characterization and representation of composite materials during processing.png)
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCESIF3.7
PREAI
分享收藏The complete amino acid sequence of rubredoxin from the green phototrophic bacterium Chlorobium thiosulphatophilum strain PM绿硫菌Chlorobium thiosulphatophilum菌株PM来源的rubredoxin的完整氨基酸序列
OAAI
OAAI分享收藏Stress-initiated void formation during cure of a three-dimensionally constrained thermoset resin
PREAI
分享收藏
查看更多内容