Superhard Tungsten Diboride-Based Solid Solutions
.png){kind=icon}
PRE
AI
DOI：10.1021/acs.inorgchem.8b02620.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Solid solutions of tungsten diboride (WB2) with increasing substitution of tungsten (W) by tantalum (Ta) and niobium (Nb)-ranging from 0 to 50 at. % on a metals basis-were synthesized through resistive arc melting. Samples were characterized using a combination of powder X-ray diffraction (PXRD) for phase identification, energy-dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy for elemental composition, Vickers microindentation for hardness measurements, and thermogravimetric analysis for thermal stability. The solubility limit was found to be less than 8 at. % for Nb and less than 10 at. % for Ta, as determined by PXRD. Vickers hardness (111,) values were measured to be 40.3 +/- 1.6 and 41.0 +/- 1.2 GPa at 0.49 N for 6 at. % Nb and for 8 at. % Ta substitution, respectively. In addition, the hardest solid solution (W0.92Ta0.08B2) showed oxidation resistance up to similar to 570 degrees C, approximately 70 degrees C higher than that of tungsten carbide (WC). Although pure WB2 is known not to be superhard, these results demonstrate the formation of superhard solid solutions through the substitution of tungsten by small amounts of transition metals. This increase in hardness can be attributed to solid solution hardening.
Keyword:
TRANSITION-METAL BORIDES
ELECTRONIC-STRUCTURE
MAGNETIC-PROPERTIES
RHENIUM DIBORIDE
W-B
TETRABORIDE
OXIDATION
HARDNESS
TEXTURE
MB2
AI总结
对已上传原文的论文进行重点信息的提取，主要内容包括：简要概述、研究摘要、背景介绍、关键亮点、图文解析、展望与总结。
期刊
IF:
4.7
论文数:
4.9W
被引数:
10.5W
机构
引用论文
Superhard Monoborides: Hardness Enhancement through Alloying in W1-xTaxB.png)
ADVANCED MATERIALS
ADVANCED MATERIALSIF26.8
PREAI
分享收藏Morphology of electropolymerized aniline films modified by para-phenylenediamine对苯二胺改性的电聚合苯胺膜的形貌
PREAI
分享收藏
查看更多内容