Understanding slip activity and void initiation in metals using machine learning-based microscopy analysis
.png){kind=icon}
OA
AI
DOI：10.1016/j.msea.2022.142738.png)
.png){kind=icon}
.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
The use of machine learning techniques to supplement traditional data analysis in mechanics and materials research can improve the understanding of microstructure-property relationships. Identification of key micro structural features or correlation between deformation mechanisms and material response can be discerned that might otherwise have been overlooked. Motivated by the possibilities of gaining additional insight into the process of void nucleation in polycrystalline metals, several machine learning techniques are applied to the analysis of mesoscopic deformation mechanisms as determined by experimental characterization and modeling. Results from crystal plasticity modeling, experimental microstructural analysis, and theoretical models of slip transmission are combined to test a hypothesis regarding fatigue-induced void nucleation. Unsupervised spectral clustering was used with results from crystal plasticity simulations to characterize slip system activity for different crystallographic orientations. The slip system activity as determined by the clustering analysis was then fed into a K-nearest neighbor classifier to quantify the probability of slip transmission across different grain boundaries of interest and analyze grains containing fatigue-induced voids. An unique and unanticipated result from the unsupervised clustering analysis shows that including a group of partially-active slip systems was more appropriate than using the binary classification of active/non-active. Predicted slip activity behavior in a face centered cubic material was shown to differ significantly from that of a body-centered cubic material due to non-Schmid effects. The outcome of the overall analysis was that grains containing fatigue-induced voids were more likely to be surrounded by grains with orientations that inhibited slip transmission according the Lee Robertson-Birnbaum (LRB) criteria. Finally, it is demonstrated that smaller datasets using limited simulation results were equally effective at predicting a similar outcome when additional physical descriptors for the slip system activity are used.
Keyword:
Machine learning
Mechanics
Fatigue
Crystal plasticity
Slip transmission
AI总结
对已上传原文的论文进行重点信息的提取，主要内容包括：简要概述、研究摘要、背景介绍、关键亮点、图文解析、展望与总结。
期刊
机构
引用论文
.png){kind=icon}
Insights into twinning in Mg AZ31: A combined EBSD and machine learning studyMg AZ31中的孪生洞察: EBSD和机器学习相结合的研究OAAI
OAAI分享收藏
查看更多内容