Abstract
En 中文
Tensile stress occurs in the vicinity of upper surface of the specimen in the severe plastic deformation zone, which increases the cracking and fracture tendency of the specimen and impedes the further ECAP processing. in this paper, the conventional ECAP die (Psi = 16 degrees and (Phi = 90) was modified to eliminate the tensile stress and enhance the compressive stress in the severe plastic deformation zone, therefore reducing the cracking and fracture tendency of the specimen. Finite element analysis demonstrated that the stress state changes from tensile to strongly compressive when using the modified die. A modified die was made and employed to extrude the commercially pure aluminum to verify its effectiveness experimentally. The billet was successfully extruded for 20 passes without obvious surface defects with the modified die, compared to 13-14 passes at most for the conventional die. Consequently, much more fine and uniform microstructure was obtained with the average grain size of 200-300 nm, while the average grain size is similar to 500 nm in the case of using the conventional die. (C) 2008 Elsevier B.V. All rights reserved.
Keywords:
Equal Channel Angular Pressing (ECAP)
Finite Element Method (FEM)
Metals and alloys
Deformation and fracture
Journal
J
IF:
7.5
Papers:
1.6W
Citations:
4.5W
Organization
Cited Papers
Equal channel angular extrusion: from macromechanics to structure formation.png)
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSINGIF7
PREAI
ShareSaveThe shearing characteristics associated with equal-channel angular pressingMATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
OAAI
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSINGIF7
OAAIShareSaveThe effect of material properties and tooling design on deformation and fracture during equal channel angular extrusionACTA MATERIALIA
ACTA MATERIALIAIF9.3
PREAI
ShareSaveShareSaveShareSave no more
no more