Cold Sintering Halide-in-Oxide Composite Solid-State Electrolytes with Enhanced Ionic Conductivity
.png){kind=icon}
PRE
AI
DOI：10.1021/acsami.4c13031.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
All-solid-state batteries (ASSBs) have attracted increasing attention for next-generation electrochemical energy storage due to their high energy density and enhanced safety, achieved through the use of nonflammable solid-state electrolytes (SSEs). Oxide-based SSEs, such as Li1.3Al0.3Ti1.7(PO4)3 (LATP), are notable for their high ionic conductivity and excellent chemical and electrochemical oxidation stability. Nevertheless, their brittle mechanical properties and poor interface contact with electrode materials necessitate high-temperature and long-duration sintering or postcalcination processes, limiting their processability for real-world applications. Additionally, the formation of secondary phases can detrimentally affect the ionic conductivity of LATP electrolytes. Emerging halide-based SSEs offer reliable deformation for practical processing while maintaining high ionic conductivity. In this work, we report a transient liquid-assisted cold sintering process to integrate oxide-based LATP as the matrix and halide-based Li3InCl6 as the conductive boundary phase into a halide-in-oxide ceramic composite electrolyte at a low processing temperature of 150 degrees C. This composite structure significantly reduces interface resistance, effectively addressing ion-transport depletion across the boundaries between LATP particles. Consequently, the cosintered LATP-Li3InCl6 composite SSE exhibits a high ionic conductivity of 1.4 x 10-4 S cm-1 at ambient temperature. Furthermore, the symmetric Li|LATP-Li3InCl6nDMF|Li cell demonstrates stable stripping and plating processes for 1600 h at 55 degrees C (0.1 mA cm-2) and 1200 h at 100 degrees C (1 mA cm-2). This work represents the first demonstration of halide-oxide ceramic composite SSEs that combine the advantages of oxides and halides for high-performance SSBs.
Keywords:
cold sintering
solid-state electrolytes
LATP
halide
composite