Cracks in functionally graded materials
.png){kind=icon}
OA
AI
DOI：10.1016/S0921-5093(03)00582-3.png)
.png){kind=icon}
.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
The weight function method is described to analyze the crack growth behavior in functionally graded materials and in particular materials with a rising crack growth resistance curve. Further, failure of graded thermal barrier coatings (TBCs) under cyclic surface heating by laser irradiation is modeled on the basis of fracture mechanics. The damage of both graded and non-graded TBCs is found to develop in several distinct stages: vertical cracking --> delamination --> blistering --> spalling. This sequence can be understood as an effect of progressive shrinkage due to sintering and high-temperature creep during thermal cycling, which increases the energy-release rate for vertical cracks which subsequently turn into delamination cracks. The results of finite element modeling, taking into account the TBC damage mechanisms, are compatible with experimental data. An increase of interface fracture toughness due to grading and a decrease due to ageing have been measured in a four-point bending test modified by a stiffening layer. Correlation with the damage observed in cyclic heating is discussed. It is explained in which way grading is able to reduce the damage. (C) 2003 Published by Elsevier B.V.
Keywords:
FGM
fracture mechanics
R-curve
residual stresses
TBC
AI Summary
Key information extracted from the uploaded paper, including a brief overview, abstract, background, key highlights, visual analysis, and future outlook.
Journal
M
IF:
7
Papers:
3.7W
Citations:
13.8W
Organization
No organization information available