Effects of Ni additions on cast and coarsened microstructure of near-eutectic Al–10Ce alloys
.png){kind=icon}
PRE
AI
A
S
D
C
P
DOI：10.1016/j.matchar.2026.116900.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
• Ni addition to near-eutectic Al–10Ce raises the liquidus temperature and broadens the solidification range. • Ni promotes grain refinement and increases the fraction of strengthening intermetallic phases. • Al–Al11Ce3–Al3Ni ternary eutectic structures form, with Al23Ce4Ni6 appearing at 5 wt% Ni. • Refined Al–Al11Ce3–Al3Ni eutectic improves strengthening efficiency.
Keywords:
Al–Ce–Ni
Cast aluminum
Eutectic structure
Solidification
Thermal stability