Environmentally assisted cracking from initiation to failure of 316 H steel under creep in saturated lead-bismuth eutectic

delete2026-08-06
delete0
PRE
AI
D
De-Cheng He
R
Run‐Zi Wang *
W
Wen-Rui Nie
W
Wen-Hu Xu
X
Xi-Yu Chen
L
Lin-Hao Gu
H
Huayan Hu
K
Kai-Shang Li
H
He Zhu
X
Xian-Cheng Zhang
S
Shan-Tung Tu
DOI：10.1016/j.corsci.2026.114167delete
deleteOriginal
deleteOriginal request for help
deleteShare
deleteSave
Abstract

Abstract

En 中文
• Environmental assisted cracking accelerates full-life creep failure in LBE. • Oxide cracking promotes surface crack initiation. • LBE-oxide coexistence reduces crack propagation resistance.

Journal

Corrosion Science cover
Corrosion Science
IF:
8.5
Papers:
1.3W
Citations:
7.3W

Organization

C
China Nuclear Power Technology Research Institute Co., Ltd.
Scholars:
55
Papers: 35
Citations: 0
E
east china university of science and technology
Scholars:
7.3K
Papers: 2.4K
Citations: 3
Cited Papers

Cited Papers

Citing Papers

Citing Papers