Experimental and Numerical Analysis of Electrospun Polylactic Acid Fiber Deposition: Effects of Processing Parameters on Morphology and Coating Uniformity
.png){kind=icon}
OA
AI
S
N
M
A
L
O
DOI：10.3390/fib14060075.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Non-uniform fiber deposition remains a critical limitation in electrospun poly(lactic acid) (PLA) coating systems. In the present study, experimental characterization was combined with numerical simulations to evaluate the influence of electrospinning parameters on fiber morphology, coating uniformity, and thickness distribution. A 3% PLA solution was electrospun under different processing conditions by varying the applied voltage, needle-to-collector distance, flow rate, and deposition time. The resulting coatings were further analyzed using numerical simulations performed with ANSYS Fluent 2020 R2 software. The results demonstrated that both solution-related and operational parameters strongly influence fiber morphology and spatial deposition behavior. Increasing the applied voltage promoted the formation of thinner fibers; however, excessively high voltage values generated jet instability associated with fiber fragmentation and spray formation. Furthermore, the deposited fibrous layers showed preferential accumulation in the central region of the collector, together with a gradual decrease in coating thickness toward the peripheral areas. A strong correlation was observed between the numerical simulations and the experimental results, confirming the reliability of the proposed modeling approach. Among the investigated conditions, the optimal electrospinning parameters were identified as an applied voltage of 16 kV, a needle-to-collector distance of 17 cm, and a flow rate of 2.5 mL/h. These conditions enabled the formation of homogeneous PLA nanofibers with minimal structural defects and improved substrate adhesion. The combined experimental and numerical approach provides valuable insight into the optimization of electrospinning parameters governing fiber formation and deposition behavior.
Keywords:
electrospinning
poly(lactic acid) (PLA)
electrospun fibers
fibrous coatings
fiber deposition
numerical simulation (ANSYS Fluent)
fiber morphology
process optimization
Journal
IF:
3.9
Papers:
810
Citations:
2.8K
Organization
Cited Papers