Exploring the tempering behaviour of additively manufactured high-alloy tool steel using synchrotron X-ray and neutron techniques
.png){kind=icon}
OA
AI
Z
X
D
P
A
D
X
C
P
B
DOI：10.1016/j.addma.2026.105219.png)
.png){kind=icon}
.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Post-processing heat treatment provides a critical pathway toward the commercialisation of additively manufactured (AM) S390 high-speed steel, which is a representative high-alloy tool steel employed in precision manufacturing, offering up to 1.5 times longer tool life and over 20% higher cutting speeds compared to conventional grades. In this study, the phase evolution of AM S390 steel during heat treatment, with particular emphasis on carbide precipitation behaviour, was systematically investigated using a combination of synchrotron X-ray and neutron techniques. The metastable M2C carbides were found to dissolve during austenitisation, while the stable primary carbides MC and M6C experienced coarsening with an average size increase of about 60 nm after just 2 min of tempering. Moreover, the austenite lattice parameters reduced from 3.618 to 3.608 within the first 10 min of tempering, suggesting carbon depletion in the steel matrix was likely associated with the formation of secondary carbides. This interpretation was substantiated by small-angle scattering results, which revealed the presence of nanoscale precipitates with a volume fraction of 3.1% after 60 min of tempering. These microstructural evolutions collectively accounted for the observed peak hardness of 921 HV. Furthermore, a comparative analysis of synchrotron and neutron small-angle scattering data highlighted the complementary strengths of each technique, offering critical insight into their suitability for characterising nanoscale features AM high-alloy steels.
Keywords:
Additive manufacturing
Steels
Tempering
Synchrotron X-ray diffraction
Small-angle scattering