Highly stable anode-free sodium batteries enabled by mechanically deformable nucleation interface
.png){kind=icon}
PRE
AI
DOI：10.1016/j.ensm.2024.103784.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Anode-free sodium metal batteries (AFNMBs) with zero excess sodium offer superior energy density, lower cell cost, and design practicality for next-generation EVs and other applications. However, reaching consistent high Coulombic efficiency (CE) greater than 99.9 % remains a challenge for this battery architecture. In this study, our findings support that using a soft Li metal interface under a current collector coated with a thin carbon black nucleation layer facilitates extremely stable nucleation and growth of Na metal by locally distributing pressure to mitigate SEI or dead sodium formation. Specifically, our findings demonstrate Na half cells with stable CE of 99.98 % over 500 cycles at 0.5 mA/cm(2). Further, zero-excess sodium full cell AFNMBs with Na3V2(PO4)(3) cathodes exhibit total first cycle formation loss of only 5.4 % at C/10 rates, which is over two times lower than commercial Li-ion cells, with capacity retention of 97.4 % after 100 cycles at 0.5 mA cm(-2) (similar to C/3) and average round-trip charge efficiency of 99.97 %.
Keywords:
Anode-free sodium metal batteries
Zero excess metal batteries
Sodium metal
Interfacial pressure
Electroplating