Interface behavior and strain localization in high‑nitrogen steel/Ti2AlNb joints brazed with a Ti–Zr–Cu–Ni filler metal
.png){kind=icon}
PRE
AI
J
Y
Y
H
X
S
H
R
X
Z
P
DOI：10.1016/j.matchar.2026.116871.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
• The multilayer interfacial structure of High‑nitrogen steel/Ti2AlNb joints is revealed. • Interfacial carbonitrides on the HNS side in brazed HNS/Ti2AlNb joints are identified for the first time. • The optimal joint performance at 940 °C is revealed. • The embrittlement mechanism of HNS/Ti2AlNb joints is revealed.
Keywords:
High-nitrogen steel
Brazing
Interface
Carbonitride