Ionic conductivity and micro structure of solid electrolyte La2Mo2O9 prepared by spark-plasma sintering

doi:10.1016/j.jeurceramsoc.2004.08.023

Ionic conductivity and micro structure of solid electrolyte La2Mo2O9 prepared by spark-plasma sintering

2005-09-01

24

PRE

AI

DOI：10.1016/j.jeurceramsoc.2004.08.023

Original

Original request for help

Save

Abstract

En 中文

Dense La2Mo2O9 ceramic electrolytes were prepared with ultrafine powder by the SPS rapid sintering method. The conductivity of the specimens by SPS was much higher than those sintered by conventional process. Moreover, the unilateral alignment of rod-type grains happened in the specimens sintered by SPS at higher temperatures or for longer holding time. The anisotropy in ionic conductivity was attribute to the directional alignment of rod-type grains. The oxygen ion conductivity parallel to the direction of rod-type grains was higher than that perpendicular to the grains. (c) 2004 Elsevier Ltd. All rights reserved.

Keywords:

La2MO2O9

spark-plasma sintering

ionic conductivity

Ionic conductivity and micro structure of solid electrolyte La2Mo2O9 prepared by spark-plasma sintering

Abstract

Journal

Organization