Low-temperature sintering of PLSZT-based antiferroelectric ceramics in reducing atmosphere for energy storage
.png){kind=icon}
PRE
AI
DOI：10.1016/j.jeurceramsoc.2023.09.053.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Due to their elevated sintering temperature, pure PLZST-based antiferroelectric ceramics are unsuitable for co -firing with copper internal electrodes as MLCC dielectric materials. In this work, PLZST ceramic materials sin -tered at low temperature in reducing atmosphere were obtained through a unique BASK glass additive and Y3+ co-doping. While the sintering temperature of ceramics is reduced to 1040 degrees C, stable defect association (Y center dot Pb,Y ' Zr) is formed by Y3+ solution entering A/B site, which effectively inhibits the increase of defect concentration and promotes ceramic sintering. The high breakdown strength of PLSZT ceramics is attributed to their compact grain and excellent insulation resistivity, which enhance their tolerance to electric fields. An ultrahigh recoverable energy density (Wrec) of 4.9 J/cm3 with a high energy storage efficiency (eta) of 92.8% are achieved at an electric field of 400 kV/cm. Moreover, the AFE ceramics possess excellent discharge energy storage properties with a high discharge energy density (Wd) of 4.4 J/cm3 and a large power density (Pd) of 125 MW/cm3.
Keywords:
PLZST
Antiferroelectric ceramic
Low temperature sintering
Reducing atmosphere