Microstructure control for developing Fe-Pd ferromagnetic shape memory alloys
.png){kind=icon}
OA
AI
DOI：10.1016/S1468-6996(02)00012-8.png)
.png){kind=icon}
.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
The effect of microstructure on the ferromagnetic shape memory effect in Fe-Pd alloys was examined focusing on the orientation distribution, the grain boundary character and the grain size. Fe-29.7-31.0 at.%Pd polycrystals composed of columnar or equiaxed grains were prepared and their magnetostriction was measured under a magnetic field up to 10 kOe. The magnetostriction of the columnar crystals was much larger than that of the equiaxed ones due to the development of < 100 > fibre texture and < 100 > tilt grain boundary. In particular, a large magnetostriction of 4.5 X 10(-4) was obtained even in the polycrystals. The grain boundaries of the columnar crystals also influenced the variant selection of martensites, resulting in strong dependence of the magnetostriction on the direction of magnetic field. Larger grain size did not always result in larger magnetostriction in Fe-Pd alloys. An increase in the grain size of the alloys was sometimes accompanied by the development of several sets of twin variants within a grain, resulting in a decrease in the magnetostriction. (C) 2002 Elsevier Science Ltd. All rights reserved.
Keywords:
Shape memory effect
Magnetostriction
Microstructure
Orientation distribution
Grain boundary character
Grain size
Strain compatibility
Variant selection