Multifunctional coating for marine applications: simultaneously achieving corrosion resistance, microwave absorption, and drag reduction via fluorosilane-encapsulated CIPs
.png){kind=icon}
PRE
AI
DOI：10.1016/j.actphy.2026.100292.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
• Our coating exhibited superhydrophobicity with a water contact angle of 158°. A drag reduction exceeding 70% was achieved at shear rates ranging from 0.1 to 100 s-1, slip length exceeding 3 mm. • Our coating exhibits an extraordinary wide absorbing band of 7.52 GHz at a thickness of 1.3 mm. • Our coating demonstrated excellent long-term corrosion resistance in a neutral salt spray environment. After 40 days of immersion in a 3.5 wt.% NaCl solution, the low-frequency impedance modulus (|Z|0.01 Hz) remained above 107 Ω·cm2.
Keywords:
superhydrophobicity
drag reduction
corrosion resistance
microwave absorption
fluorosilane-encapsulated CIPs