Quantitative analysis of toughening effect of crack deflection on Si3N4/Si2N2O composites through improved indentation method
.png){kind=icon}
PRE
AI
DOI：10.1016/j.ceramint.2017.10.128.png)
.png){kind=icon}
Original request for help.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
In this study, Si3N4/Si2N2O composite ceramics prepared by hot pressing were used as an example, and the material fracture morphology and fracture mechanism were analyzed. Based on the formula of fracture toughness measured by an indentation method, a quantitative computation method was proposed to determine the toughened effect of ceramic materials resulting from the crack deflection by the second phase. The grain size and sintering density are increased with the increase of sintering temperature. The toughening effects resulting from the crack deflection is increased, and the main mode of fracture is transformed into the transgranular fracture. The Si2N2O grains can play a role in the toughening process because these grains can hinder the cracks extending along the radial direction. However, when the cracks extend in the axial direction, the toughening effect of Si2N2O grains is not obvious because of the internal stacking faults in the axial direction. The improved indentation method can quantitatively analyze the toughening effect of the second phase of composite ceramics, and the validity of this method are verified by comparing the fracture toughness of Si3N4/Si2N2O and fine grained beta-Si3N4 ceramics.
Keywords:
Si3N4/Si2N2O
Toughening
Fracture morphology
Fracture toughness
Improved indentation method