Rare-Earth modified biodegradable Zn alloys with high strength and enhanced osteogenesis
.png){kind=icon}
OA
AI
DOI：10.1038/s41467-026-74069-x.png)
.png){kind=icon}
.png){kind=icon}
Share.png){kind=icon}
Save
Abstract
En 中文
Achieving high strength and robust osteogenesis simultaneously remains a challenge for biodegradable orthopedic materials. Here we show that incorporating trace rare-earth (RE) elements into a Zn-Li-Mn system bridges this gap. By forming REZn11-13 intermetallic phases, we engineer a bimodal grain structure that elevates tensile strength to 772 MPa and bending strength to 1207 MPa, approaching the level of medical-grade titanium alloy (Ti-6Al-4V) while retaining biodegradability. Crucially, these phases act as “potential-buffering” electrodes, ensuring uniform degradation and controlled zinc ion release. This optimized ion concentration activates the Rap1 signaling pathway, resulting in twofold greater bone regeneration compared to titanium alloy implants. By integrating ultrahigh mechanical strength with potent bioactivity, this Zn-Li-Mn-Y alloy provides a superior platform for next-generation load-bearing implants, offering a degradable alternative to permanent metallic fixations. Low mechanical strength limits biodegradable orthopaedic implant use. Here, the authors develop a biodegradable Zn-Li-Mn-Y alloy approaching the strength of medical grade titanium alloy implants that promotes bone healing by controlled ion release.
AI Summary
Key information extracted from the uploaded paper, including a brief overview, abstract, background, key highlights, visual analysis, and future outlook.
Journal
IF:
15.7
Papers:
9.2W
Citations:
91.2W
View more organizations