Enhancing protonic ceramic electrolysis cell performance through electrolyte composition optimization
.png){kind=icon}
PRE
AI
DOI：10.1016/j.ceramint.2024.05.192.png)
.png){kind=icon}
原文求助.png){kind=icon}
分享.png){kind=icon}
收藏
摘要
En 中文
Polarization resistance, chemical stability against high steam, and faradaic efficiency (FE) are important parameters for steam electrolysis using protonic ceramic electrolysis cells (PCEC) at an intermediate temperature range of approximately 500 degrees C. To investigate the effects of electrolyte composition on these parameters, PCECs were fabricated using two electrolyte compositions: one without Zr, Ba(Ce0.8Y0.1Yb0.1)O3-delta (BCYYb), and one with Zr, Ba(Ce0.3Zr0.5Y0.1Yb0.1)O3-delta (BCZYYb), as well as a double-layered electrolyte BCYYb/BCZYYb. Although Zr in BCZYYb is required for chemical stability, BCYYb without Zr can also be chemically stable against high steam at 500 degrees C. Additionally, BCYYb has a higher conductivity compared to BCZYYb, which contributes to lower ohmic resistance and the highest peak power density in H2 fuel at 700 degrees C (2.04 W/cm2) among the cells with three different electrolytes. However, the BCYYb electrolyte exhibits a slightly higher polarization resistance than BCZYYb. In PCEC operation at 500 degrees C, the electrolyte composition significantly affects the FE. At a high current density (0.8 A/cm2), the FE of the PCEC with the BCYYb electrolyte (85 %) is significantly larger than that with BCZYYb (68 %).
Keyword:
Protonic ceramics
Steam electrolysis
Faradaic efficiency
Protonic ceramics electrolysis cells
PCECs
Green hydrogen
期刊
IF:
5.6
论文数:
5.0W
被引数:
15.5W
机构
引用论文
Mixed proton and electron conducting double perovskite anodes for stable and efficient tubular proton ceramic electrolysers用于稳定高效的管状质子陶瓷电解槽的质子和电子导电混合双钙钛矿阳极.png)
NATURE MATERIALS
NATURE MATERIALSIF38.5
PREAI
分享收藏Stability of BaCeO3-based proton conductors in water-containing atmospheresBaCeO3-based质子导体在含水气氛中的稳定性
PREAI
分享收藏Water solubility, proton and oxygen diffusion in acceptor doped BaCeO3: A single crystal analysisSOLID STATE IONICS
SOLID STATE IONICSIF3.3
PREAI
分享收藏分享收藏
查看更多内容